UTILIZATION OF WASTE PLASTIC IN FLEXIBLE PAVEMENTS
M. Bheem Reddy1, E. Mahendhar Reddy2, G. Sai kumar Reddy3
1,2,3Student, Department of Civil Engineering, Sree Dattha Institute of Engineering and Science, Telangana, India
----------------------------------------------------------------------***---------------------------------------------------------------------
Abstract - Plastic are typically organic polymers of high molecular mass and often derived from petro-chemicals and
becoming a major problem in causing environmental pollution when it burns. They were widely used because of their
ease in manufacturing, low cost, and versatility. Utilization of these waste material like plastic bags, bottles, etc by
partial replacement of bitumen in bituminous mixes to improve the properties of mix in addition to solving disposal
problems. The waste plastic like bottles, plastic glasses were used are cleaned and cut into pieces of size ranges from
2.36mm to 75 microns and sieved. These pieceswereaddedevenly aroundthehot aggregatesandheatedupto160℃and
heating the bitumen up to 130℃. The resultant mix was used in the flexible road construction. It also increases theroad
life and also as well as help in decrease of pollution to the Environment. Plastic roads are very useful in the hot climatic
areas. By using of this type of waste plastic in the construction of pavement can increase the strength, durability etc., by
which the bituminous pavementsarefailing.Bituminousmixisacompositematerialmostly usedinconstructionprojects
like road surfacing, parking lots etc., It consists of bitumen (used as a binder) and mineral aggregate which are mixed
together and laid down in layers then compacted.
Key Words- Waste plastic, Environmental pollution, Partial replacement, Bituminous mix, Bituminous pavements.
1. INTRODUCTION
Plastic is a synthetic material made from a wide range of organic polymers such as polyethylene, PVC, nylon, etc., that can be
moulded into shape and then set into a rigid or slightly elastic form. Plastics are durable, cheaper and degrade very slow. The
chemical bonds that make plastic to degrade vary slowly and it is a great threat to environment. The municipal solid waste
contains mixture of bio- -degradable and non-biodegradablesolids.The non-biodegradablesolidsconsistsofplasticintheform
of bottles, carry bags etc. The waste plastic is used as to make binders stiff which reduces the rutting, thermal cracking,
stripping, cost of maintenance of pavement. It improves the fatigue resistance, bituminous pavement durability, reducingcost
of laying pavement and reducing the pollution. The majority of waste plastic is polyolefin which includes high density
polyethylene (HDPE), linear low density polyethylene (LLDPE), polypropylene (PP) and high molecular weight polyethylene
(HMWP). The waste plastic modified bituminous mix gives more service, nopotholes,lessfailuredueto rutting,etc.,Becauseof
several reasons the polymer modified bitumen mix is used in laying pavements.
Rapid growth of industries, increase in the population, increase inthevehiculartraffic,thelayersof bituminous roadsplays
a vital role in facing the heavy loads. So, the bituminous surface layer experiences a great impact of heavy loading. The surface
layer should be modified in bringing more service life for pavement. The use of modified bituminous surface layers are
important to be implemented. This plastic modified bitumen mix is also economic and doesn’t cause any environmental
pollution.
This paper gives the proper utilization of waste plastic in bituminous mix to enhancethepavement performance,minimize
the bitumen cost by giving more service life and to protect the environment. In this study we are conducting Marshall Stability
test to increase slip resistance and resistance against seasonal variations.
1.1. OVERVIEW OF THIS RESEARCH
Several researches have been made to protect the environment in inventingseveral thingsandthis modifiedbitumenprovides
a very long life and economically low cost. Polymer-modified bitumen is the one of the invention in saving the environments
and above mentioned factors. This modified bitumenisthealternatetotheconventional bitumenconcretewhichdoesn’tutilize
much bitumen and increases the binding property of bitumen. The elastic nature of plastic stiffens the bond between
aggregates and bitumen.
1.2 PAST RESEARCH ON THIS PROJECT
Dr. Rajagopalan Vasudevan, Indian chemistry professor had made a wide research on using the waste plastic and awarded
with one of India’s highest civilian awards, The “Padma Shri”, for his ground-breaking researchonre-usingthewasteplasticin
a very unusual way and regarded as “Plastic Man of India”.

2. International Research Journal of Engineering and Technology (IRJET) e-ISSN: 2395-0056
Volume: 06 Issue: 10 | Oct 2019 www.irjet.net p-ISSN: 2395-0072
© 2019, IRJET | Impact Factor value: 7.34 | ISO 9001:2008 Certified Journal | Page 1439
2. LITERATURE REVIEW
3. OBJECTIVES
The main research of this research is to utilize the waste plastic in bituminous pavements as it is causing environmental
pollution.
The objectives of this research which we have to achieve are
• The optimum use of plastic in bituminous pavements at which it gains maximum strength and durability properties.
• The comparison of conventional bituminous mix and polymer-modified bituminous mix.
• To reduce the plastic disposal problems.
The counties like Netherlands, United Kingdom, Australia Indonesia, etc are also has the plastic-modified roads.
3.1. COLLECTION OF PLASTICS
The plastic is collected from the municipal agencies. This plastic should be having the softening point which is greater than
bitumen and its melting points should be between 160℃ –170℃ is collected. This plastic should be cleaned to remove any
organic or waste materials and shredded to the size between2.36mmto75microns. Thusthedensityoftheplasticfibershould
be around 0.4-0.5g/cc which is so small when compared to bitumen.
Types of plastic which can be used are:
 PP(polypropylene)
 PET(polyethylene)
 HDPE(high density polyethylene)
 LDPE(low density poly ethylene)
 PS(polystyrene)
S.NO. AUTHOR TITLE CONCLUSION
1. Ms. Jamdade P. K., Mr.
Patil RaviKiran, Mr
.Patil Prathik, Mr.
Rajurwar Rohit, Mr.
Loya Tushar, Mr.Shaik
Amer, Mr. Shaik Alfaiz
Use of waste plasticin
flexible pavement
road construction
Concluded that the penetration and ductility resistance of
modified bitumen sample increases within the range of 0-12%
when the plastic of 8.4% is added to conventional bitumen mix
and air voids decreases so as increases the percentage of plastic
2. Sasane Neha. B.,
Gaikwad. Harish., Dr. J
R Patil and Dr. S D
Khandekar
Application of waste
plastic as an effective
construction material
in flexible pavement
Concluded that increase of wasteplasticinbitumenincreasesthe
properties of aggregates and bitumen, the optimum content of
plastic used can be done up to 10%
3. Yash Menaria and
Rupal Sankhla
Use of waste plasticin
flexible pavements-
Green Roads
Discussed about the comparison of various properties of
conventional bitumen and polymer-modified bitumen. The test
results show the improved properties of polymer-modified
bitumen.
4. Miss Apurva J Charan Use of plastic wastein
flexible pavements
Concluded that the properties of aggregates are improved.
Stripping value is reduced to nil and water absorption also
reduced to nil.
5. Plastic roads Ahmed Trimbakwala Concluded that the binding property of plastic waste

3. International Research Journal of Engineering and Technology (IRJET) e-ISSN: 2395-0056
Volume: 06 Issue: 10 | Oct 2019 www.irjet.net p-ISSN: 2395-0072
© 2019, IRJET | Impact Factor value: 7.34 | ISO 9001:2008 Certified Journal | Page 1440
Fig.1: Waste Plastic
 PVC (poly vinyl chloride) is not used because its melting point is very high. Because of this reason PVC is not used.
4. METHODOLOGY
The methodology contains step by step procedures of testing of individual materials for the quality analysis, preparation and
testing of conventional and modified-bituminous samples by the Marshall mix design and testing is done by Marshall stability
test. Firstly, the tests related to materials-aggregates, bitumen, filler materials are done and the quality of each material is
checked as per recommendations of code. Generally, the plastic is added into mix in twoways,wetmixanddry mix. Inwetmix,
the shredded plastic fibers are added directly into the hot bitumen and mixed with hot aggregates and laid on the ground. In
dry mix, the aggregates are heated to a temperature of 165-175 degree Celsius and then this shredded plastic is added and
mixed with hot bitumen and is laid on the ground. Generally dry mix is the most preferred one as compare to wet mix.so we
follow dry mix. The plastic which is coated around the aggregates doesn’tallowthewatertoflowthroughtheaggregateswhich
gives the durability, high stability value and high stripping value. The dry process is more preferred because theresultswhich
we got related to strength and durability criteria are more. So, we adopt dry process. Then this mix is made for testing with
Marshall Stability test. Place the polymer-modified bitumen into the moulds. For comparison we have to make 3 trials on 3
different specimens of conventional bitumen(0% plastic),polymer-modified bitumen(5% plastic),polymer-modified
bitumen(7% plastic) and polymer-modified bitumen(10% plastic).So, totally we have to make 12 moulds of two different
bituminous mixes as mentioned above.
Fig.2: Aggregates and plastic materials used
Fig.3: Types of plastic to be used

4. International Research Journal of Engineering and Technology (IRJET) e-ISSN: 2395-0056
Volume: 06 Issue: 10 | Oct 2019 www.irjet.net p-ISSN: 2395-0072
© 2019, IRJET | Impact Factor value: 7.34 | ISO 9001:2008 Certified Journal | Page 1441
Fig.4: Plastic coated aggregates and plain aggregate
Fig. 5: Materials Fig.6: heating of mix
Fig.7 &8: Marshall Stability Specimen moulds
Fig 9: mould filled with Fig 10: Marshall Stability
bituminous mix machine
Table: Materials and their quality tests as per Indian Standards
S.NO MATERIALNAME SPECIFICATIONS TEST ON MATERIALS
1. Bitumen Penetration grade-
60/70, 80/100
Viscosity-VG-30
Penetration Test [1202-1978]
Softening Point
[ 1205-1978]
Ductility Test[1208-1978]
2. Aggregates Size- 20mm,
10mm
Sieve analysis [IS 2386-part-1]
Aggregate impact test[IS 2386 part-4]

5. International Research Journal of Engineering and Technology (IRJET) e-ISSN: 2395-0056
Volume: 06 Issue: 10 | Oct 2019 www.irjet.net p-ISSN: 2395-0072
© 2019, IRJET | Impact Factor value: 7.34 | ISO 9001:2008 Certified Journal | Page 1442
Aggregate crushing value test [IS
2386- part-4]
Water absorption [IS 2386-part-3]
4 Plastic Plastic passing
through 4.75mm
sieve and retained
on 2.36mm sieve
Sieve analysis
RESULTS AND ANALYSIS
Table 1: Physical properties of bitumen as per IS 73-1992 [1]
S.NO Description Test results Permissible limits Test method
1. Specific gravity of bitumen 1.05 0.99 (minimum) IS 1202-1978
2. Softening point of bitumen 52.3℃ 47℃ IS 1202-1978
3 Flash point of bitumen 270 220 IS 1209-1978
4 Fire point of bitumen 305 270 IS 12091978
5 Bitumen penetration test 50mm 45mm IS 1203-1978
6. Ductility test 94cm 100cm IS 1208-1978
Table: Aggregate test results
S.NO Description Test
results
Permissible
limits
Test method
1. Aggregate impact value test 24.50 Max. 30% IS 2386-part-2
2. Specific gravity of
aggregates (20mm)
2.63 IS 2386- part-
3
3. Specific gravity of
aggregates (10mm)
2.56 IS 2386-part-3
4. Specific gravity of
aggregates (6mm)
2.5 IS 2386-part-3
5. Specific gravity of
aggregates (stone dust)
2.46 IS 2386-part-3
6. Stripping value of
aggregates
4.6% 5% Physical
appearance
7. Water absorption 0.52 Max 2% IS 2386 part-3
Stability vs Plastic content:
Table: Stability values with respect to % of plastic content
S. No % Plastic Added Avg. Stability Values Of 3 Specimens, kg
1 0 995
2 5 1043
3 7 1097
4 10 1122
5 12 1023
 From the above table it is clear that as % of plastic is increasing in the mix, the stability value increases.
 The optimum plastic content should be 10%.

6. International Research Journal of Engineering and Technology (IRJET) e-ISSN: 2395-0056
Volume: 06 Issue: 10 | Oct 2019 www.irjet.net p-ISSN: 2395-0072
© 2019, IRJET | Impact Factor value: 7.34 | ISO 9001:2008 Certified Journal | Page 1443
Graph: Stability vs % plastic
900
950
1000
1050
1100
1150
0 5 7 10 12
% Plastic
Stability,kg
Air voids with respect to Plastic content:
Table: Air voids with respect to Plastic content
S.NO. % plastic Air voids, %
1 0 4.5
2 5 3.7
3 7 4.2
4 10 5.4
5 12 5.2
Graph: air voids vs % plastic
0
1
2
3
4
5
6
0 5 7 10 12
% plastic
Airvoids,%
As per above graph, it is clearthat the air voids increases with respect toplasticcontentbecausetheplasticweaddedisattached
around the rough surface of the aggregates. Due to this, the air voids are expecting to increase. This plastic layer decreases the
flow of water between the aggregates will decreases.
Flow value vs % plastic
Table: Flow value vs % Plastic
S. No % Plastic Flow Value (0.25 mm)
1 0 2.8
2 5 2.75
3 7 2.71
4 10 2.65
5 12 2.60

7. International Research Journal of Engineering and Technology (IRJET) e-ISSN: 2395-0056
Volume: 06 Issue: 10 | Oct 2019 www.irjet.net p-ISSN: 2395-0072
© 2019, IRJET | Impact Factor value: 7.34 | ISO 9001:2008 Certified Journal | Page 1444
Graph: flow value vs % plastic
2.5
2.55
2.6
2.65
2.7
2.75
2.8
2.85
0 5 7 10 12
% Plastic
Flow Value,
0.25mm
CONCLUSION:
Bituminous plastic is used for the better performance of roads. This helps to havea better bindingofbitumenwasteplastic and
aggregate due to increased bonding and increased area of contactbetweenpolymersandbitumen. ThePlasticmixalsoreduces
the voids. This prevents the moisture absorption and oxidation of bitumen by entrapped air. Resultsreducingrutting, raveling
and there is no pothole formation. The roads can withstand heavy traffic and show better durability.
ACKNOWLEDGEMENT
This piece of work would never be accomplished without God almighty. For it is under grace that I live, learn and flourish. this
report owes its existence to help, support and inspiration of our H.O.D. Dr. Ashwin Raut and our guide Gunti Umashanker,
M.tech (transportation Engineering). They are constant source of enthusiasm and encouragement during the entire research.
We also owe this research report to our family members. Throughout all over endeavours, their love, support, guidance and
endless patience have truly inspirational- “Thanks will never suffice”.
We are graceful to the faculty and staff of department of Civil Engineering, Sree Dattha Institute of Engineering and Science,
Hyderabad for their support.
REFERENCES
[1] Yash Menaria and Rupal Sankhla, “Use of Waste Plastic in Flexible Pavements--Green Roads”.
[2] Brajesh Mishra, “A Study On Use Of Waste Plastic Materials in Flexible Pavements”.
[3] Miss Apurva J charan, “Use of Plastic waste in flexible pavements”.
[4] Ahmed Trimbakwala, “Plastic Roads”.
[5] Sasane Neha. B., Gaikwad. Harish., Dr. J.R. Patil and Dr. S D Khandekar, “Application of Waste plastic as an effective
construction material in flexible pavement”.
BIOGRAPHIES:
B. Tech (Civil Engineering),
Sree Dattha Institute of
Engineering and Science,
Hyderabad, Telangana, India.

8. International Research Journal of Engineering and Technology (IRJET) e-ISSN: 2395-0056
Volume: 06 Issue: 10 | Oct 2019 www.irjet.net p-ISSN: 2395-0072
© 2019, IRJET | Impact Factor value: 7.34 | ISO 9001:2008 Certified Journal | Page 1445
B. Tech (Civil Engineering),
Sree Dattha Institute of
Engineering and Science,
Hyderabad, Telangana, India.
B. Tech,(Civil Engineering),
Sree Dattha Institute of
Engineering and Science,
Hyderabad, Telangana, India.