Liquid penetrant inspection is one of the oldest and most widely used non destructive testing methods. It is also called as dye penetrant inspection.Penetrant testing can be applied to most of materials including metallic and non metallic objects.This Presentation will gives you an overview about Liquid Penetrant Testing and Various methods used for Inspection
1. Module II
Introduction to Liquid Penetrant Testing
13-09-2017 Hareesh K ,AP ME,DOME,VAST 1
Hareesh K Nair
Assistant Professor
Department of Mechanical Engineering
2. Liquid Penetrant Testing
โข Liquid penetrant inspection
is one of the oldest and
most widely used non
destructive testing methods.
It is also called as dye
penetrant inspection.
13-09-2017 Hareesh K ,AP ME,DOME,VAST 2
3. Liquid Penetrant Testing
(continue)
โข Penetrant testing can be applied to most of materials
including metallic and non metallic objects
โข Metallic materials include aluminum, magnesium, titanium, cast iron,
stainless steel, powdered metal products, copper, brass, bronze, etc.
โข Non metallic materials include ceramics, plastic, molded rubber,
composites, glass, etc.
โข Penetrant testing canโt be applied on a porous surface
13-09-2017 Hareesh K ,AP ME,DOME,VAST 3
4. Penetrant Testing History
โข Penetrant first used in 1900s to detect cracks in locomotive parts
โข The method was called oil and whiting
โข The method used dirty lubricating oil that was thinned with kerosene followed
by application of chalk coating which absorbed oil from the cracks
โข In 1940s fluorescent or visible dye was added to the oil
13-09-2017 Hareesh K ,AP ME,DOME,VAST 4
5. โข Penetrants
โข The penetrants are mixtures
of organic solvents, which are
characterized their ability to
wet materials, spread rapidly
and penetrate into minute.
โข Developer
โข Developer is good absorbent
material capable of drawing
traces trapped penetrants from
the discontinues back into
surfaces. It also provide a
light background to increase
contrast when visual penetrant
is used
13-09-2017 Hareesh K ,AP ME,DOME,VAST 5
6. Principles
โข Clean & dry test object
โข Apply penetrant and let it penetrate
โข Remove excess penetrant
โข Apply developer
โข Evaluate indications
โข Post clean test object
13-09-2017 Hareesh K ,AP ME,DOME,VAST 6
7. Types of Penetrants
โข Basically Penetrants are classified as Based on
1. Physical Properties
i) Fluorescent Penetrants
ii) Visual penetrants
i) Fluorescent penetrants are generally green in colour
and they contain dye that glow brightly when exposed
to UV lights
ii) Visual penetrants are usually red in colour that provide
high contrast against the white developer background
13-09-2017 Hareesh K ,AP ME,DOME,VAST 7
8. 2. Based on removal technique
i) Solvent removable
Ii)Water washable
Iii)Post emulsifiable
i) Solvent Removable
In this method , Penetrants are removed by wiping
with a cloth dampened with solvent
13-09-2017 Hareesh K ,AP ME,DOME,VAST 8
10. ii) Water Washable / WW
โข Have a built in
emulsifier, easily
removed by water rinse
โข Typical rinse procedure
are (refer to manual):
Pressure < 40 psi
Temperature 10o - 38o C
Angle 45o - 75o
13-09-2017 Hareesh K ,AP ME,DOME,VAST 10
11. iii) Post Emulsifiable / PE
โข Not contain emulsifying agent, not
soluble in water
โข Emulsifier applied to remove excess
penetrant by dipping, spraying, or
flowing
โข Emulsifier dwell time is 1 - 4
minutes
โข Penetrant โ emulsifier mixture
isremoved by water rinse
โข There are 2 types of emulsifier,
lipophilic and hydrophilic
13-09-2017 Hareesh K ,AP ME,DOME,VAST 11
12. Lipophilic Emulsifier
โข Mechanism of lipophilic emulsification is by diffusion
โข Both molecules of emulsifier and penetrant penetrate each other to
form a washable mixture
โข Rate of diffusion increases as concentration and temperature raised
13-09-2017 Hareesh K ,AP ME,DOME,VAST 12
13. Hydrophilic Emulsifier
โข Is a water based solution, mixture of chemical called surfactant
โข Works based on principle of peeling the penetrant
โข Need pre-rinsing prior to emulsifier application to help remove 60 โ
80 % penetrant and provide an even surface
โข Applied by immersion or spraying
13-09-2017 Hareesh K ,AP ME,DOME,VAST 13
14. 3 Based on Strength Indication
โข i) Level ยฝ- Ultra Low sensitivity
โข ii) Level 1- Low Sensitivity
โข iii) Level 2- Medium Sensitivity
โข Iv) Level 3- High Sensitivity
โข V) Level 4- Ultra High Sensitivity
13-09-2017 Hareesh K ,AP ME,DOME,VAST 14
15. Properties of Good penetrant
1. Capillarity
It is the ability of a liquid to flow in narrow
spaces without the assistance of external forces. This
property helps the penetrant to fill a void.
13-09-2017 Hareesh K ,AP ME,DOME,VAST 15
16. Contact Angle
Angle formed by the solid-liquid interface and liquid
โ vapour interface measured from the side of a liquid
is called contact angle.
Mostly the liquid penetrant has contact angle of 0deg
13-09-2017 Hareesh K ,AP ME,DOME,VAST 16
17. 3. Viscosity
โข Viscosity is the internal resistance of a liquid to
flow. The penetrants with less viscosity fill the
cracks in time
13-09-2017 Hareesh K ,AP ME,DOME,VAST 17
18. 4. Surface Tension
โข Surface tension is nothing but wetting capability of
a liquid. Penetrant should have good wetting
capability to spread over the surface
13-09-2017 Hareesh K ,AP ME,DOME,VAST 18
19. 5. Cohesiveness and Adhesiveness
โข The attractive force between like molecules and
unlike molecules called cohesiveness and Adhesive
forces respectively
13-09-2017 Hareesh K ,AP ME,DOME,VAST 19
20. 6. Specific Gravity
โข Specific gravity is the ratio of the density of a liquid
to the density of the standard liquid. Penetrant have
Sp Gravity less than one
13-09-2017 Hareesh K ,AP ME,DOME,VAST 20
22. Characteristics of Good Penetrants
โข It should spread easily over the surface being inspected
โข It should be easily drawn into discontinuities by
capillary action
โข It should not be harmful to the inspector or the material
being tested
โข It should possess high indicating capability
โข It should remain in fluid state
โข It should Possess less dwell time
โข It should not affect the physical and chemical properties
of the testing material
โข It should be cohesive, Adhesive and relatively low in
cost
13-09-2017 Hareesh K ,AP ME,DOME,VAST 22
23. Properties of Good developer
โข It should have good absorption characteristics
โข It should have a good contrast background
โข It should be able to uniformly cover the surface with
the thin smooth Coating
โข It should be chemically inert with test material
โข It should provide a good contrast background for
bright and clean indications
โข It should be non toxic
โข It should be easy to remove after inspection
13-09-2017 Hareesh K ,AP ME,DOME,VAST 23
24. Types of Developers
1. Dry Powder Developers
2. Water Suspendable developers
3. Water soluble developers
4. Non-aqueous developers
13-09-2017 Hareesh K ,AP ME,DOME,VAST 24
25. 1 Dry Powder Developers
โข It is a mix of light feathery powder that clumps
where penetrant bleeds back to the surface in order
to produce very defined indications
13-09-2017 Hareesh K ,AP ME,DOME,VAST 25
26. 2 Water- Suspendable Developer
โข Water suspendable developers consist of insoluble
developers particles suspended in water. Water
suspendable developers require frequent stirring to
keep the particle from setting out of suspension
13-09-2017 Hareesh K ,AP ME,DOME,VAST 26
27. 3. Water Soluble developer
โข Water soluble developer is a crystalline powder that
forms a clear solution when mixed with water.
โข The solution recrystallizes on the suraface when the
water is drained
13-09-2017 Hareesh K ,AP ME,DOME,VAST 27
28. 4. Non Aqueous
โข Non Aqueous developer suspend the developer in a
volatile solvent.
โข It is supplied by a spray gun or aerosol can and it Is
most sensitive developer for inspecting small areas
13-09-2017 Hareesh K ,AP ME,DOME,VAST 28
29. Basic Processing Steps of a Liquid
Penetrant Inspection
1. Pre-clean part.
This can range from grinding and wire brushing to merely wiping the part
with a rag moistened with the cleaner/ remover. The surface needs to be
free of dirt, rust, scale, paint, oil, and grease, and be smooth enough to wipe
off the penetrant without leaving residue
13-09-2017 Hareesh K ,AP ME,DOME,VAST 29
30. 2. Penetrant Application:
Once the surface has been thoroughly cleaned and dried, the
penetrant material is applied by spraying, brushing, or
immersing the part in a penetrant bath
13-09-2017 Hareesh K ,AP ME,DOME,VAST 30
31. 3. Penetrant Dwell:
The penetrant is left on the surface for a sufficient time to allow as much
penetrant as possible to be drawn from or to seep into a defect. Penetrant
dwell time is the total time that the penetrant is in contact with the part
surface. Dwell times are usually recommended by the penetrant producers
or required by the specification being followed. The times vary depending
on the application, penetrant materials used, the material, the form of the
material being inspected, and the type of defect being inspected for.
Minimum dwell times typically range from five to 60 minutes. Generally,
there is no harm in using a longer penetrant dwell time as long as the
penetrant is not allowed to dry. The ideal dwell time is often determined by
experimentation and may be very specific to a particular application.
13-09-2017 Hareesh K ,AP ME,DOME,VAST 31
32. 4. Excess Penetrant Removal:
This is the most delicate part of the inspection procedure because the
excess penetrant must be removed from the surface of the sample while
removing as little penetrant as possible from defects. Depending on the
penetrant system used, this step may involve cleaning with a solvent, direct
rinsing with water, or first treating the part with an emulsifier and then
rinsing with water
13-09-2017 Hareesh K ,AP ME,DOME,VAST 32
33. 5.Developer Application:
A thin layer of developer is then applied to the sample to draw
penetrant trapped in flaws back to the surface where it will be visible.
Developers come in a variety of forms that may be applied by dusting
(dry powdered), dipping, or spraying (wet developers).
13-09-2017 Hareesh K ,AP ME,DOME,VAST 33
34. 6.Evaluate indications.
It is critical to examine the part within the time frame designated in the written
procedure. Length of an indication can grow over time as penetrant bleeds out,
causing an acceptable indication to be a rejectable defect. Length of indication
is measured for evaluation, not length of the flaw. Here, the two linear
indications are rejectable defects. The round indication is non relevant.
13-09-2017 Hareesh K ,AP ME,DOME,VAST 34
35. 7. Post-clean part.
The part needs to be cleaned to remove all developer
after it has been evaluated.
13-09-2017 Hareesh K ,AP ME,DOME,VAST 35
36. Penetrant Test Methods
Commonly used penetrant testing methods are
1) Water Washable Method
2) Post Emulsifiable Method
3)Solvent Removable Method
13-09-2017 Hareesh K ,AP ME,DOME,VAST 36
37. Interpretation of Results
SL
NO
Defect Descripton
1 Casting Porosity Spherical surface Indications
2 Casting Cold Shut Dotted lines
3 Cracks Staight continuous surface lines
4 Hot tears Ragged line of variable width
5 Heat treat Cracks Multiple irregular lines
6 Thermal cracks interconnecting lines
7 Lack of fusion Broken line of varying width
8 Fatigue cracks continues line in parts
13-09-2017 Hareesh K ,AP ME,DOME,VAST 37
38. False Indications
A false indication is an accumulation of penetrant caused by a
drop of penetrant left on the workpiece.
However, there are two conditions which may create
accumulations of penetrant that are sometimes confused with
the true crack and discontinuities
The first includes indications caused by poor washing and the
other one may created where parts press fir to each other.
If a wheel press fit onto a shaft, penetrant will show an
indication at the fit line
But these types of indications are easy to identify since they
are regular in form and shape
13-09-2017 Hareesh K ,AP ME,DOME,VAST 38
40. Typical applications of Liquid penetrant
Inspection
1. Aerospace :Typical Components that are checked by this method
include Turbine, rotor disc, blades, aircraft wheels, Casting, forged
parts and welded assemblies
2. Automobiles: Many automotive parts particularly aluminium
castings and forging including pistons and cylinder heads are
subjected to this form of quality checks before assembly
3. Railways: LPI to detect fatigue cracking is also used for the
regular in service examination of the bogie frames of railway
locomotive and the rolling stock
4. Tool and dies: field drilling rays, drill pipes, castings and drilling
equipment's inspected by this methods
5.Inspection on reactors and tank: Tanks, vessels, reactors, piping,
dyers in the chemical, petro-chemical industries.
13-09-2017 Hareesh K ,AP ME,DOME,VAST 40