1. Product profile :
Toughtop 20 is two component chemically curing aliphatic acrylic polyurethane coating. It has a glossy finish with very
good gloss retention. It is a high solids, high build product. It is fast drying. It can be used direct to metal. The coating is
highly flexible, impact resistant and has excellent adhesion. To be used as topcoat in atmospheric environments.
Polyurethane coating (also known as PU coating) on metal provides exceptional weathering performance
characteristics. This coating, commonly referred to as poly coating, is used in virtually all industrial markets to provide a
smooth durable finish that has superior resistance to corrosion, abrasion, and chemical exposure. Polyurethanes are
normally used to topcoat high build epoxy and inorganic zinc.
Tobslak Toughtop 20
Polyurethane coating for metal protection
PROPERTY PROFILE :
A high performance finishing coat for structural steel in aggressive and corrosive environments such as onshore and
offshore steel superstructures, pipelines and bridges etc. Also suitable as a finishing coat for concrete surfaces where
high durability is desired.
Easy maintenance coating with long term recoatability properties.
Excellent colour and gloss retention.
Excellent flow and levelling properties.
Resistant to spillage or splashes of mild chemicals.
Able to achieve a film build of 75µm in a single coat application.
Excellent UV resistance and overall durability properties.
Application examples:
Recommended for refineries, power plants, bridges, buildings , offshore environments and mining equipments.
SURFACE PREPERATION : For optimum performance, this product should be applied to a surface that has been blast
cleaned and suitably primed and built (e.g. with Zifo Primer or Miscoat MIO) • For recoating application, underlying
system should be sound and undamaged. • Ensure that the surface to be over-coated is clean, dry, and free from dust,
grease and oil, or any other surface contaminants. • Always ensure the maximum over-coating time for the primer or build-
coat has not been exceeded prior to application.
APPLICATION :
Stir base thoroughly then mix four parts base and one part hardener by volume to uniform consistency. Allow the mixture
to mature for 20-30 min. and stir again before application & occasionally during use to prevent settling of metallic zinc.
For Brush, Roller, Airless spray application, no thinning is required. In conventional spraying, 5% thinning is recommended
for ease of application.
NOTE:
1) Use the mixed paint within specified pot life period.
2) Do not apply at temperatures below 10° C or at high relative humidity, above 90% or during rain, fog or mist.
3) Brushes & spray equipment should be cleaned with Thinner Toblux-102 TT (Maximum 5% addition) .
The product can be applied by Spray: Use airless spray. Brush: Recommended for stripe coating and small areas. Care
are must be taken to achieve the specified dry film thickness.
Art. No. AR 90-10033
Page 1 of 2
2. Page 2 of 2
For further safety information, please refer to our Material Safety Data Sheet (MSDS)
INDIA
Tobslak India Pvt. Ltd.
305-c, 3rd floor, Irishtech park,sect-48,sohna road,
Gurugram-122018(HR),INDIA
Email: ccin@tobslak.com, www.tobslak.com
GERMANY
Tobslak International,Eschersheimer Landstraße 42,
60322, Frankfurt am Main, Hessen,
Germany ,Phone:(+49) 3221 1226423
Email:info@tobslak.com; www.tobslak.com
Important: The descriptions, designs, and data contained
herein are presented for your guidance only. Because there
are many factors under your control which may affect
processing or application/use it is necessary for you to make
appropriate tests to determine whether the product is
suitable for your particular purpose prior to use. NO
WARRANTIES OF ANY KIND, EITHER EXPRESS OR IMPLIED,
INCLUDING WARRANTIES OF MERCHANTABILITY OR FITNESS
FOR A PARTICULAR PURPOSE, ARE MADE REGARDING
PRODUCTS DESCRIBED OR DESIGNS, OR INFORMATION SET
FORTH, OR THAT THE PRODUCTS, DESIGNS, OR DATA MAY BE
USED WITHOUT INFRINGING THE INTELLECTUAL PROPERTY
RIGHTS OF OTHERS. IN NO CASE SHALL THE DESCRIPTIONS,
DATA OR DESIGNS PROVIDED BE PRESUMED TO BE A PART OF
OUR TERMS AND CONDITIONS OF SALE. Further, you expressly
understand and agree that the descriptions, designs, and data
furnished by TOBSLAK hereunder are given gratis and
TOBSLAK assumes no obligation or liability for same or results
obtained from use thereof, all such being given to you and
accepted by you at your risk.
TYPICAL COATING SPECIFICATION
Substrate Priming 2nd Coat 3rd Coat 4th Coat
STEEL ZIFO Primer Midcoat MIO Toughtop 20 Toughtop 20
Volume Solid 60% (based on ASTM D2697)
Mixing ratio by Volume Base : Hardener 6.4 : 1
Individual shelf life 8 months in sealed condition & at ambient temp.
Application by Brush, Airless spray, Roller or Conventional spray
Theoretical Coverage 11-12 m²/l.
Flash Point above 28°C
Finish Semi-gloss, Low sheen & Matt
Packing 20 litres set (17.28 litres Base : 2.72 litres Hardener)
Colour RAL Shades
Dry Film Thickness Range 50 µm to 75 µm
Wet [μm] Dry [μm]
85 50
PHYSICAL PROPERTIES
Theoretical Coverage