- 1. International Journal of Advanced Research in Engineering and Technology (IJARET), ISSN 0976 –
6480(Print), ISSN 0976 – 6499(Online) Volume 5, Issue 2, February (2014), pp. 128-137, © IAEME
128
AN ECO-FRIENDLY RUBBER-TEXTILE COMPOSITES FOR
CONSTRUCTION OF RUBBER DAM TO USE IN WATERSHEDS
APPLICATION
K. Rajkumar, P. Thavamani, Chandresh Dwivedi*, PankajRegar
Indian Rubber Manufacturers Research Association (IRMRA), Plot No 254/ 1B, Road No. – 16V,
Wagle Industrial Estate, Thane, India 400604
ABSTRACT
Rubber dam is a unique rubber-textile composite, in which technical textiles acts as
reinforcing and strength providing material, whereas rubber acts as shock absorber and water
proofing material. Basically Rubber dam consists of rubber-textile composite sheet, concrete base,
anchoring system, inflation deflation device (pump). In rubber textile composite, rubber to fabric
adhesion plays the most critical role for determining assembly process and ultimate strength of
product. A vulcanizable adhesive for rubber to fabric fabrication of composite material was
developed which was compatible with rubber as well as fabric. Evaluation of bonding system with
respect to peel strength, breaking strength, shear adhesion strength, types and design (weave pattern)
of fabrics, were the major determining criteria for selection and optimization of fabric for Rubber
Dam application. Thus the optimized adhesive system has been developed with the characteristics of
high adhesive strength and good compatibility with rubber as well as with fabric. The potential
application of these technical textiles with natural rubber composites is in the development of rubber
dam. Rubber Dams are resistant to abrasion, corrosion, earthquake, radiation and these require zero
maintenance. Weave patterns of fabrics is also an important criteria for Rubber to fabric adhesion;
thus Mockleno weave pattern gives better adhesion strength with rubber than Honeycomb and Matt
weave patterns. Layout of composite sheet was optimized on the basis of breaking strength and peel
strength. Nylon fabrics are polar in nature, so gives better adhesion than non-polar Polyester fabrics.
Bonding adhesive systems for treatment of fabrics were developed such as Resorcinol-
Formaldehyde-Latex (RFL) for Nylon 6, 66 and Grillbond (Blocked poly iso-cyanate) for Polyester
fabrics. Rubber compounds for cover layer and cushion/friction layer were optimized on the basis of
required properties such as tensile strength, tear strength, elongation at break, hardness, ageing
resistance, water resistance etc. Various types of Nylon 6, 66 fabrics were tried with natural rubber
for peel strength and bonding evaluation and one was optimized according to best required properties
INTERNATIONAL JOURNAL OF ADVANCED RESEARCH IN ENGINEERING
AND TECHNOLOGY (IJARET)
ISSN 0976 - 6480 (Print)
ISSN 0976 - 6499 (Online)
Volume 5, Issue 2, February (2014), pp. 128-137
© IAEME: www.iaeme.com/ijaret.asp
Journal Impact Factor (2014): 4.1710 (Calculated by GISI)
www.jifactor.com
IJARET
© I A E M E
- 2. International Journal of Advanced Research in Engineering and Technology (IJARET), ISSN 0976 –
6480(Print), ISSN 0976 – 6499(Online) Volume 5, Issue 2, February (2014), pp. 128-137, © IAEME
129
for Rubber Dam application. Trials with polyester fabrics were also taken due to various advantages
of polyester fabrics such as low cost, easy availability and low moisture regain over Nylon fabrics.
To overcome the adhesion problem with polyester fabric, a special chemical treatment was given.
Keywords: Natural Rubber, Technical Textiles (Nylon6, Nylon 66, Polyester Fabrics), Adhesive,
Adhesion, Composite, Rubber Dam.
INTRODUCTION
Technical textiles have attracted considerable attention and technical textiles were widely
used to encompass all textile products other than those intended for apparel, household and
furnishing end uses. Industrial textiles are now more often viewed as a subgroup of a wider category
of technical textiles, referring specifically to those textile products used for industrial application
such as filters, machine clothing, conveyor and v-belts, inflatable products for marine application
abrasive substrates etc. In the composites industry, woven, knitted, braided, non-woven and wound
yarn reinforcement made from glass, carbon fiber and organic polymer materials such as Nylon,
Polyesters, Aramid are all now widely used.
Polyamide (Nylon) and Polyester fabrics are extensively used as reinforcing material for
flexible rubber composites such as fan belts, hoses, flexible drivers, tires and other applications.
They account for 28 and 48% of the total synthetic fiber production. Woven fabrics exhibit good
stability in the warp and weft directions and offer the highest yarn packing density in relation to
fabric thickness. The adhesion of fabric to rubber plays the most critical role to ensure the life of the
flexible composite of rubber dam. To impart good bonding between rubbers to technical textile, an
adhesive must not only hold materials together but also withstand operating loads and also be
resistant to operating medium to ensure the life of the product. In this context a good bonding agent
or adhesive and its concentration should be optimized with respect to types of fabrics, weaving
pattern and gsm.
We tried different types of Nylons, Polyester fabrics for the evaluation of natural rubber to
fabric adhesion. Nylon fabrics have good impact resistance, breaking strength and flexibility. Due to
higher polarity, Nylon fabric should have a better adhesion compared to polyester fabric. Whereas
Polyester fabric is less flexible than Nylon but has better breaking strength and excellent moisture
resistance. Nylons have a limitation for moisture absorption when used in dampen environment. The
adhesion property of the polyester fabric was further enhanced by activating its surface.
Rubber dams are inflatable and deflectable hydraulic structures. Thousands of rubber dams have
been installed worldwide for various purposes: irrigation, water supply, power generation, tidal
barrier, flood control, environmental improvement, and recreation. Furthermore, rubber dams have
been used in cold areas where the temperature is as low as – 40°C. The simplicity and flexibility of
the rubber dam structure and its proven reliability are key considerations in its wide scope of
applications. The total investment cost of rubber dams being about 40% lower than the conventional
gated regulating structure, the utility of the same is much greater in as much as it addresses the age
old problems of flood, droughts, low water efficiency, excessive dependence on monsoon etc.
EXPERIMENTAL
Materials
Carbon black (SRF N774) was supplied by M/s Specialty Carbon and Chemicals Ltd,
Mumbai. Rubber chemicals like antioxidants and accelerators were supplied by M/s Vinhar
chemicals Pvt. Ltd., Mumbai. Zinc oxide, Stearic acid and Sulphur were supplied by M/s
RubbosynthImpex Pvt.Ltd., Mumbai. Natural Rubber (RSS-4) was supplied by M/s Shreeji
- 3. International Journal of Advanced Research in Engineering and Technology (IJARET), ISSN 0976 –
6480(Print), ISSN 0976 – 6499(Online) Volume 5, Issue 2, February (2014), pp. 128-137, © IAEME
130
Enterprises, Mumbai. All the fabrics were supplied by M/s Kusumgar Corporates, Mumbai. Dry
bonding agents (Cohedur RK and Cohedur A250 as shown in table 2) were supplied by M/s Lanxess
India Ltd., Mumbai. Silica and DEG were supplied by M/s B.P Chemicals, Mumbai. Formulations of
rubber compounds are given in tables 1 and fabric types are given in tables 2, 3 and 4.
Preparation of Samples
Six different types of cushioncompounds (three with and three without dry-bonding agent)
were prepared. Compounding was done using open two roll mixing mill. 15-20% rubber solution
was prepared in solvent xylene, under stirring condition and was applied on the treated fabrics by
spray gun technique. Two different set of Nylon fabrics were tested (Nylon 6 and Nylon 66), i.e. nine
type Nylon-6 and nine type Nylon 66 samples were tested. Testing sample specimens were made as
per layout using compression moulding technique.
Processing parameters were determined on the basis of rheometric studies of cushion
compounds. Sheet of cushion compound of thickness of 3 mm was applied on both the sides of
coated fabric and was molded at 150ºC with required optimum curing time as per rheometric studies
data. Peel strength was measured as per test method ASTM D 413, tensile properties were measured
as per ASTM D 412 and ageing properties was measured as per ASTM D573.
Formulations of rubber compounds
Table 1 shows, formulations of NR based cushion compounds without dry bonding and with
dry bonding. Total six different types of cushion compounds were prepared, three without dry
bonding(DN1, DN2, DN3) and three with dry bonding (DN*1, DN*2 and DN*3) by adding two
types of dry bonding in them, DB Cohedur RK and DB Cohedur A250 with 3 and 4 phr
respectively.
Table 1. Formulations of NR cushion compounds (Phr)
Raw Materials (Phr) DN*1 DN*2 DN*3 DN1 DN2 DN3
NR (RMA-IX) 100 100 100 100 100 100
Zinc Oxide 6 6 6 6 6 6
Stearic Acid 1 1 1 1 1 1
TDQ 1 1 1 1 1 1
SRF N 774 25 30 20 25 30 20
Silica VN3 15 10 20 15 10 20
DEG 0.5 0.5 0.5 0.5 0.5 0.5
CI Resin 5 5 5 5 5 5
DB Cohedur RK*
0 0 0 3 3 3
DB Cohedur A250*
0 0 0 4 4 4
CBS 1 1 1 1 1 1
Sulphur 2 2 2 2 2 2
Total 156.5 156.5 156.5 163.5 163.5 163.5
Composition of dry bonding agents:-
*DB Cohedur RK (Dry bonding agent, Component-1):- Resorcinol-Silica blend or equivalent
*DB Cohedur A250 (Dry bonding agent, Component-2):-HMT/Hexamethylenetetramine
(Formaldehyde donor)-Silica blend or equivalent.
- 4. International Journal of Advanced Research in Engineering and Technology (IJARET), ISSN 0976 –
6480(Print), ISSN 0976 – 6499(Online) Volume 5, Issue 2, February (2014), pp. 128-137, © IAEME
131
Details of Nylon 6, Nylon 66 and Polyester fabrics used
Table 2, 3 and 4 shows, details of Nylon 6, Nylon 66 and Polyester fabrics used in present
study with their fabric types, weave pattern, GSM, breaking strength and finished width. Honeycomb
and Mockleno are open type weave patterns while Matt is closed type weave pattern.
Table 2. Details of RFL treated Nylon-6 fabrics used in present study
Fabric types Weave pattern GSM
Thickness
(mm)
Breaking Strength
Kg/5cm
Warp Weft
3297 Matt 342.2 0.54 628 615
3298 Honeycomb 346.6 0.60 600 608
3299 Mockleno 355.9 0.58 617 629
3300 Matt 450.5 0.69 761 759
3301 Mockleno 451.5 0.85 736 735
3302 Honeycomb 457.9 0.85 706 723
3303 Matt 571.4 0.85 967 958
3304 Mockleno 569.8 1.05 848 846
3305 Honeycomb 583.0 1.05 862 852
Table3. Details of RFL treated Nylon-66 fabrics used in present study
Fabric types Weave pattern GSM
Thickness
(mm)
Breaking Strength
Kg/5cm
warp weft
3360 Matt 418.5 0.76 710.4 651.2
3361 Honeycomb 15.5 0.97 696.8 628.1
3362 Mockleno 410.9 0.95 741.8 664.5
3363 Matt 540.5 1.00 990.8 796.2
3364 Mockleno 550.1 1.23 981.4 864.2
3365 Honeycomb 533.1 1.31 930.5 838.7
3366 Matt 655.9 1.09 1178.0 944.9
3367 Mockleno 672.1 1.31 1142.0 998.0
3368 Honeycomb 676.8 1.51 1157.0 995.0
- 5. International Journal of Advanced Research in Engineering and Technology (IJARET), ISSN 0976 –
6480(Print), ISSN 0976 – 6499(Online) Volume 5, Issue 2, February (2014), pp. 128-137, © IAEME
132
Table 4. Details of Grillbond treated Polyester fabrics used in present study
Fabric types Weave pattern GSM Finished width (m)
M2AP1 Matt 350 1.46
M2AP2 Honeycomb 350 1.40
M2AP3 Matt 550 1.37
M2AP4 Honeycomb 550 1.32
M2AP5 Matt 450 1.50
M2AP6 Honeycomb 450 1.50
M2AP7 Matt 450 1.30
Details of formulations of adhesive systems (RFL and Grillbond) used for treatment of fabrics
Table 5, shows typical formulation of Resorcinol-Formaldehyde-Latex (RFL) adhesive for
treatment of Nylon 6 and Nylon 66 fabrics and Table 6 shows, Grillbond (Blocked Poly-iso-cyanate)
adhesive for treatment of Polyester fabrics.
Table 5. Typical formulation of RFL based adhesive treatment for Nylon fabrics
Component Parts (Wet) Parts (Dry)
Resorcinol 9.4 9.4
Formalin (37%) 13.8 5.1
Sodium hydroxide (10%) 7.0 0.7
Water 157.8 --
VP latex (40%) 212.0 84.8
Water 100.0 --
Total 500.0 100.0
Table 6. Typical formulation of pre -dip for Polyester fabric based on Grillbond
(Blocked Poly-isocyanate)
Component Parts (Wet) Parts (Dry)
Blocked poly- isocyanate# (40%
dispersion)
180.0 72.0
Epoxy resin^ 27.2 27.2
Gum tragacanth solution (2%) 25.0 0.5
Dispersant (50%) 0.6 0.3
Water 1767.2 --
Total 2000.0 100.0
# Grillbond IL6, a caprolactum blocked methylene bis (phenyl di-isocyanate)
^ Decancol NER 010a, a liquid epoxy resin derived from epichlorohydrin and glycerol
- 6. International Journal of Advanced Research in Engineering and Technology (IJARET), ISSN 0976 –
6480(Print), ISSN 0976 – 6499(Online) Volume 5, Issue 2, February (2014), pp. 128-137, © IAEME
133
RESULTS AND DISCUSSION
Peel strength of different fabrics with rubber compounds has been tested and their bonding
evaluation occurred. Table 8 shows, the peel strength of nylon-6 without dry-bonding system. As the
peel strength are not adequate certain additives was included in rubber formulation to promote
adhesion directly with the fabric and these are, in-situ or direct/dry bonding systems. These systems
rely on the inclusion into the rubber matrix of resorcinol (or a resorcinol/formaldehyde pre-
condensate) together with a methylene donor. The addition of these two components will give a
moderate level of adhesion. The original methylene donor used for this system was
hexamethylenetetramine. While this was perfectly adequate as a methylene donor from the adhesion
point, it also significantly affected the cure system, and thus alternative materials have been used,
especially hexamethoxy methyl melamine. Comparing Table 8 and Table 9, it is clear that peel
strength has increased with addition of dry bonding agent. DN3 compound was optimized
considering its Optimum cure time, Tensile strength, Elongation at break, Hardness and Tear
strength.From Table 9, it has been observed that in all the fabrics, peel strength are higher in weft
direction. This implies that rubber to fabric bonding is better in weft direction. This may be justified
by the facts that, fabrics are more stretched in warp direction because of the stretching at the time of
fabric manufacturing. So, when frictioning of rubber into fabric occurs, the penetration of rubber into
woven fabric is more in the weft direction than in warp direction. This increases the adhesion
strength or peel strength in weft direction.
Comparing Tables 8, 9, 10 and 11, Nylon 6 fabrics gives better peel strength than Nylon 66
fabrics. We have also tried with different polyester fabrics for bonding evaluation. However, in order
to achieve satisfactory levels with polyester, it is necessary to use a pre-treated polyester yarn. Peel
strength of RFL treated polyester fabrics was very low, but after treatment of these fabric with
Grillbond (Blocked polyisocyanate), we got very good adhesion strength.
The dry-bonding systems can be used alone, with untreated fabrics. However, if they are used
in conjunction with adhesive dipped fabrics, both systems will contribute to the adhesion, and
achieved levels can be significantly higher than with either system alone.
From Table 15, it is clearly shown that 100% VP latex (in RFL) treated Nylon 6 and Nylon
66 fabrics shows higher peel strength than 50-50% SBR latex treated and 100% SBR latex treated
fabrics.
Table 7, shows rheological and physico-mechanical properties of NR based friction
compounds without and with dry bonding. From the table, it has been concluded that DN3 friction
compound shows highest tensile strength and other physical properties so it was optimized as friction
compound for Rubber Dam application.
Table 7. Rheological and Physico-mechanical properties of NR based friction compounds without
and with dry bonding agent (Cured at 150°C)
Property Unit DN*1 DN*2 DN*3 DN1 DN2 DN3
Optimum cure time Min. (150ºC) 15 17 18 9.4 8.6 18
Tensile strength MPa 26 27 27 20 24 29
Elongation at Break % 680 680 730 520 510 630
Hardness Shore A 52 58 55 65 62 64
Tear Strength Kg/cm 72 58 69 58 46 72
- 7. International Journal of Advanced Research in Engineering and Technology (IJARET), ISSN 0976 –
6480(Print), ISSN 0976 – 6499(Online) Volume 5, Issue 2, February (2014), pp. 128-137, © IAEME
134
Table 8. Peel Strength (Kg/cm) of RFL treated Nylon-6 fabrics (Warp direction) with friction
compounds, DN*3 (without dry bonding)
Nylon 6 fabrics (RFL
treated)
DN*1 DN*2 DN*3
Average
3297 3.3 3.6 3.3 3.4
3298 5.7 4.2 5.1 5.0
3299 3.9 2.7 4.2 3.6
3300 3.6 3.2 3.8 3.5
3301 4.4 3.7 5.0 4.3
3302 5.9 4.9 5.4 5.4
3303 3.9 1.6 4.2 3.2
3304 3.6 3.5 4.5 3.8
3305 5.6 4.6 6.4 5.5
Table 9. Peel strength (Kg/cm) of RFL treated Nylon 6 fabrics with DN3 friction compound (with
dry bonding agent)
Nylon-6 fabrics (RFL
treated)
Peel Strength (Kg/cm)
Weft direction Warp direction Average
3297 7.3 6.7 7.0
3298 7.0 6.8 6.9
3299 6.8 6.0 6.4
3300 8.8 6.1 7.4
3301 7.4 6.9 7.1
3302 8.0 8.9 8.4
3303 9.4 4.2 6.8
3304 4.8 5.8 5.3
3305 8.5 7.0 7.7
Table 10. Peel strength (Kg/cm) of RFL treated Nylon 66 fabrics with DN*3 friction compound
(Without dry bonding)
Nylon-66 fabrics (RFL
treated)
Peel strength (Kg/cm)
Weft direction Warp direction Average
3360 3.7 2.0 2.8
3361 4.7 5.2 4.9
3362 5.8 5.0 5.4
3363 4.7 5.2 4.9
3364 5.6 4.5 5.0
3365 4.6 5.5 5.0
3366 5.4 3.4 4.4
3367 4.3 4.1 4.2
3368 5.6 4.2 4.9
- 8. International Journal of Advanced Research in Engineering and Technology (IJARET), ISSN 0976 –
6480(Print), ISSN 0976 – 6499(Online) Volume 5, Issue 2, February (2014), pp. 128-137, © IAEME
135
Table 11. Peel strength (Kg/cm) of RFL treated Nylon 66 fabrics with DN3 compound (With dry
bonding)
Nylon – 66 fabrics (RFL treated) Peel strength in warp direction (Kg/cm)
3360 5.7
3361 5.2
3362 5.0
3363 5.2
3364 4.5
3365 5.5
3366 3.0
3367 4.0
3368 4.2
Table 12 shows, comparative peel strength of different types of polyester fabrics treated
with RFL and Grillbond. From table, it is concluded that peel strengths of Grillbond treated polyester
fabrics is much higher than the RFL treated and shows good bonding with rubber compound.
Table 12. Comparative peel strength (Kg/cm) of Polyester fabrics (RFL treated and Grillbond
treatment) with DN3 cushion compound (With dry bonding)
Polyester fabrics
Average Peel strength, Kg/cm
(RFL treated)
Average Peel strength, Kg/cm
(Grillbond treated)
M2AP1 1.8 5.2
M2AP2 2.3 6.7
M2AP3 1.9 4.7
M2AP4 1.7 4.6
M2AP5 2.5 7.8
M2AP6 2.0 6.3
M2AP7 1.8 5.8
Figure 1. Comparative peel strength of Polyester fabrics treated with RFL and Grillbond
0
2
4
6
8
10
M2AP1 M2AP2 M2AP3 M2AP4 M2AP5 M2AP6 M2AP7
Averagepeelstrength(Kg/cm)
Polyester fabric types
Average peel strength (RFL treated)
Average peel strength (Grillbond treated)
- 9. International Journal of Advanced Research in Engineering and Technology (IJARET), ISSN 0976 –
6480(Print), ISSN 0976 – 6499(Online) Volume 5, Issue 2, February (2014), pp. 128-137, © IAEME
136
Average peel strength of all Grillbond treated fabrics is much higher than RFL treated one.
Table 13. Peel strength of fabrics treated by SBR latex and VP latex with different proportion
Fabric code Fabric type Treatment type
Average peel strength
(kg/cm)
3301 Nylon 6 100 % VP Latex 11.1
3301 Nylon 6 VP:SBR (50:50) Latex 9.9
3301 Nylon 6 100 % SBR Latex 7.4
3364 Nylon 66 100 % VP Latex 9.8
3364 Nylon 66 VP:SBR (50:50) Latex 7.9
3364 Nylon 66 100 % SBR Latex 6.1
Figure 2. Comparative Peel strength of VP latex treated, VP-SBR latex treated and SBR latex
treated Nylon 6 and Nylon 66 fabrics
CONCLUSION
1. For improving rubber to fabric adhesion, dry bonding agent is required in rubber compound in
suitable proportion.
2. Nylon fabrics gives better adhesion with NR friction compound with dry bonding than compound
without dry bonding.
3. It has been also observed that, Nylon 6 fabric gives better adhesion than Nylon 66 fabric with NR
based friction compound.
4. Nylon fabrics give better adhesion than Polyester fabrics with rubber compounds.
5. Weaving pattern and direction of the fabric type also plays an important role for the adhesion.
Fabrics with Mockleno weave pattern shows better adhesion strength than honeycomb and matt.
Fabrics used in weft direction shows better adhesion strength than used in warp direction.
6. VP latex treated Nylon fabrics gives better adhesion with DN3 (with dry bonding agent)
compound compared with SBR latex treated Nylon fabrics.
7. DN3 compound was selected as a best cushion compound on the basis of required properties.
8. Dry bonding agent gives better adhesion with RFL treated fabrics.
0
2
4
6
8
10
12
Nylon6 (3301) Nylon 66 (3304)
100% VP latex VP:SBR(50:50) latex
100% SBR latex
- 10. International Journal of Advanced Research in Engineering and Technology (IJARET), ISSN 0976 –
6480(Print), ISSN 0976 – 6499(Online) Volume 5, Issue 2, February (2014), pp. 128-137, © IAEME
137
9. VP latex treated Nylon fabric gives better result compared with RFL treated fabric, even without
dry bonding agent.
10. Grillbond (Blocked Poly-isocyanate) treated Polyester fabrics shows improved adhesion strength
than RFL treated polyester fabrics.
REFERENCES
1. P. Roy Choudhury, S. K. Chakraborty, ManasiNath “Rubber Dam a novel approach for
control of water flow in water shed management for agricultural growth of India”, published
in Rubber India, vol LX, No 8, pg 49, August 2008.
2. P. Roy Choudhury,ManasiNath, BhagabatBhuyan “Design and Development of Rubber
Dam – a farmer friendly rubber reservoir”, published in Rubber Chem Review, vol. XXXVII
No. 6, pg. 29, July- August 2008.
3. P. Roy Choudhury, S. K. Chakraborty, ManasiNath “Bonding evaluation of technical textile
with rubber for rubber dam application” published in technical proceedings of 5th
International Conference a/c Rubber Expo IRE 09, on 28th
– 31st
January, 2009, Kolkata,
organized by All India Rubber Industries Association and Kharagpur IIT, pg 155.
4. P. Roy Choudhury, S. K. Chakraborty and PankajRegar, “Engineering Aspects of Innovative
Rubber Dams for Watersheds”, published in ‘Rubber Chem Review’, vol. XXXX No.5, Pg
36, May-June 2011.
5. D. Wootton in “Handbook of Rubber Bonding”, Bryan Crowther, Ed., Rapra Technology
Ltd., Shropshire, UK, 2003.
6. Paper on “The adhesion of Polyester textile to rubber” published in Rubber world Jan 02
page 21 by Song Yuexian, Wang Youdoo and XuChuanxiang, Xian Jiatong University.
7. X. Q. Zhang, P.W. M. Tam and W Zheng (2002). Construction, Operation and maintenance
of rubber dams, Can J. Civ. Eng, 29 (3): 409-420.
8. M. K. Talukdar, S. K. Chattopadhyay, and B.P Pal, “Design and Development of Fabric
Substrate for Flexible Rubber Dams” presented in The International Conference on Technical
Textiles and Nonwovens, organized by IIT Delhi, from 11 to 13th
November 2008.
9. S. K. Chattopadhyay, M. K. Talukdar and A. K. Bharimalla, “Application of Technical
Textile in Fabricating Flexi dam for Water Management in Agriculture”, National seminar on
“Non Conventional Applications of Textiles”, 11 Dec. 2010, held at CIRCOT, Mumbai.
10. D. Wootton in “Handbook of Rubber Bonding”, Bryan Crowther, Ed., Rapra Technology
Ltd., Shropshire, UK, 2003.
11. M. Lee in “Encyclopedia of Composites, vol 2” Wiley, NY, 1998.
12. A. F. Richards in “Synthetic Fibres” J.E. Mclntyre, Ed., UK, 2005.
13. ASTM D 412-98a. (1998). Fordetermination of the physico-mechanicalproperties using a
fully computerized Instron tensile testing machine 5586.
14. N.Ganesan, Bharati Raj, A.P.Shashikala and Nandini S.Nair, “Effect of Steel Fibres on the
Strength and Behaviour of Self Compacting Rubberised Concrete”, International Journal of
Civil Engineering & Technology (IJCIET), Volume 3, Issue 2, 2012, pp. 94 - 107,
ISSN Print: 0976 – 6308, ISSN Online: 0976 – 6316.
15. M. Venu and P. N. Rao, “Study of Rubber Aggregates in Concrete: An Experimental
Investigation”, International Journal of Civil Engineering & Technology (IJCIET), Volume 1,
Issue 1, 2010, pp. 15 - 26, ISSN Print: 0976 – 6308, ISSN Online: 0976 – 6316.